一、先稱取5g專用無煙煤,再稱取1g試樣(yang)煤樣(yang),
放(fang)入(ru)坩(gan)堝稱準 到(dao)0.001g。
二(er)、攪(jiao)拌(ban)(ban)(ban):用(yong)攪(jiao)拌(ban)(ban)(ban)絲將坩(gan)(gan)堝(guo)(guo)的混合(he)樣(yang)攪(jiao)拌(ban)(ban)(ban)2min,將坩(gan)(gan)堝(guo)(guo)作(zuo)45°,左右傾(qing)斜,逆時(shi)鐘方向轉動(dong),約(yue)(yue)15r/min ,攪(jiao)拌(ban)(ban)(ban)絲按同樣(yang)傾(qing)斜角(jiao)作(zuo)順時(shi)針方向轉動(dong),約(yue)(yue)150r/min ,攪(jiao)拌(ban)(ban)(ban)時(shi),攪(jiao)拌(ban)(ban)(ban)絲的圓環接觸坩(gan)(gan)堝(guo)(guo)壁(bi)與(yu)底(di)相連(lian)接的圓弧部分,經1min45s后,一邊(bian)繼續攪(jiao)拌(ban)(ban)(ban),一邊(bian)將坩(gan)(gan)堝(guo)(guo)壁(bi)與(yu) 攪(jiao)拌(ban)(ban)(ban)絲逐漸轉到垂(chui)直位置,經2min 后,攪(jiao)拌(ban)(ban)(ban)結束。
三、在(zai)攪(jiao)拌(ban)時(shi),應該防(fang)止煤樣外濺,攪(jiao)拌(ban)后(hou),將坩堝壁上煤粉輕(qing)(qing)輕(qing)(qing)掃下(xia),用攪(jiao)拌(ban)絲(si)仔細將混合(he)煤樣撥平,比坩堝的(de)層面(mian)略低(di)1—2mm,以便壓塊將混合(he)物壓緊后(hou),使煤樣表(biao)面(mian)處于同一平面(mian)。
四、用鑷子加壓塊于坩堝中心,然后將其置(zhi)于壓(ya)力器壓(ya)30s,加(jia)壓(ya)時防止沖擊(ji),加(jia)壓(ya)結束后,壓(ya)塊仍留在(zai)混合樣上(shang),加(jia)上(shang)坩(gan)堝蓋。注意(yi):從攪拌開始(shi),帶有混合煤樣的坩(gan)堝,應(ying)該輕拿輕放(fang),避免受到撞擊(ji)與振動(dong)。
五、將帶(dai)蓋的(de)坩(gan)堝(guo)放(fang)在(zai)坩(gan)堝(guo)架中,用平鏟托起坩(gan)堝(guo)架,放(fang)入預先升溫到850°c的(de)馬(ma)弗爐恒溫區,關閉爐門,6min內爐溫,應該恢復到850°c ,從放(fang)入坩(gan)堝(guo)開始(shi)計時,焦化15min 。
六、將坩(gan)堝(guo)從(cong)爐中取出,放置冷卻到室溫,取出壓塊(kuai),當壓塊(kuai)上附有焦(jiao)時,應該刷下坩(gan)堝(guo)內,稱量焦(jiao)渣(zha)總量,然后轉鼓(gu)。
七(qi)、進入第(di)一次(ci)(ci)轉鼓,把焦(jiao)塊用1mm圓孔篩進行(xing)篩分,再稱取篩上部分的(de)質量(liang),然后(hou)進行(xing)第(di)二次(ci)(ci)轉鼓試驗,重復篩分,稱量(liang)操作(zuo),每次(ci)(ci)操作(zuo),每次(ci)(ci)轉鼓5min即250r, 稱量(liang)準確至0.01g。粘結計算(suan):g=10+(30m1+70m2)/m
試(shi)中:m---焦化處理后焦渣總(zong)質量(liang)
M1---第一次轉(zhuan)鼓試驗(yan)后,篩上部(bu)分的(de)質量g
M2---第二次轉(zhuan)鼓試驗后(hou),篩上部分的質量g
八、補充試驗:當測得g<18時,需重做試驗,此時,試驗煤樣和無煙煤的比例為3:3,即3g專用無煙煤與3g的試驗煤樣,試驗步驟相同。
九、結束計算:G=(30m1+70m2)/5m